Concrete Admixture Polypropylene Monofilament Fiber
May 12, 2018

Concrete Admixture Polypropylene Monofilament Fiber Basic Info

  • Model NO.: Elt-PPMF

  • Material: 100% Polypropylene

  • Fiber Type: Staple

  • Polypropylene Staple Fiber Color: White

  • Function: High Strength Fiber

  • Length: 4,6,8,12,16,18,20,24,28,30mm ,Times of 4mm or 6mm

  • Crack Elongation: 20+/-5%

  • Polypropylene Staple Fiber Raw Material: 100% Vigin Polypropylene

  • Tensile Strength(MPa): 450 Min.

  • Melting Point(C Deg.): 160 - 170

  • Specification: CE

  • HS Code: 5503400000

  • Polypropylene Staple Fiber Usage: Concrete

  • Feature: Reinforcement

  • Pattern: Plaid

  • Width: 20um

  • Structure: Monofilament

  • Density(g/cm3): 0.91+/-0.01

  • Product Name: Polypropylene Monofilament Fiber

  • Acid &Alkali Resistance: Strong

  • Polypropylene Staple Fiber Water Absorbency: No

  • Application: Reinforcement

  • Transport Package: 0.6kg or 0.9kg a PE Bag, 18kg/ Plastic Woven Bag

  • Origin: China

Concrete Admixture Polypropylene Monofilament Fiber Product Description

1,Polypropylene Monofilament Fiber Description:
EltFiber-PPMN monofilament fiber was produced by referring foreign advanced technology for fiber spinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force. It is suited to reinforce and crack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall etc.

2,Polypropylene Monofilament Fiber Specification

Raw Material :PolypropyleneCrack Elongation:20+/-5%
Fiber Type :monofilamentFiber Diameter:20um-30um
Melting Point(C Deg.) :160 - 170  Density(g/cm3) :0.91+/-0.01
Acid &Alkali Resistance :StrongTensile Strength(MPa):450 min.
Length:4,6,8,10, 12, 16,18,20etc. times of 4 or 6mmwater absorbency :  NO


3, Polypropylene Monofilament Fiber packing:
A,600g or 900g or 1000g / pe film bag, 18kg/ Plastic woven bag,8tons/1x20`gp,20tons/40"HQ
B,600g or 900g or 1000g / pe film bag,18kgs/carton,7.2tons/1x20`gp
C,Water soluble bag is available also.

4,Polypropylene Monofilament Fiber Applications:
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.

5,Typical physical properties:
(1 )Polypropylene Monofilament Fiber Functions:
A.Resist to shrink & crack
B.Increase seepage resistance
C.Increase friction resistance
D.Increase freezing & thawing resistance
E.Improve tendons protection
F.Replace steel net (using in plastering)
G. Prevent mortar split and crackle expansion H.Increase impact resistance and peeling resistance
(2)Polypropylene Monofilament Fiber Features:
A).No agglomeration and easily spread around in mortar or concrete. Guarantee the property of crack resistance effectively
B).Apply conveniently. No need to change the proportion of mortar, and just put the fibers into the mortar mixture and stir for a moment after adding water.
C).Has fine economic property. The equivalent dia. of polypropylene monofilament is only φ 0.02mm, so the ratio of dia. And surface is high and on the basis of crack resistance, it can reduce the amount (0.6kg/m 3 ) and cut down the cost effectively.
D).Be better to plaster. Because a great number of thin fibers spread into mortar evenly, so the plastering is much easier and this can improve the binding strength between surface and base.
E).The fiber has stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.
Our other concrete fiber :

6,Polypropylene Monofilament Fiber Applying Instruction:
A).Dosage: for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar Is enough, and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B).Stirring requirement: The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely.
Also it can be mixed with cement and other aggregates in advance, stirring by adding water at worksite before construction.
Our Advantage
1).Why AEI
A. SGS verified suppliers
B. CE certificate offered
C. Professional suppliers with rich export experience
D. Small order / OEM order acceptable
E. Full-time tracking your orders
F. One-stop solutions to you, such as Hotel reservations,Factory visiting or Auditing, Sourcing, Quality control, Warehousing & Logistics service, customs declaring and tracking your order continuously.

2),we handle orders as SGS management system ,and issue report after shipment to customer.
A.Test DATA report will be sent to you asap after cargo ready for shipment.
B.While loading container , pictures will be took as SGS inspection process
a.Empty container                           b.The first layer of shipment
c.loading half of container               d.full of container before close to the door
e.seal of container f.container seal lock with number
After pics are took ,Container loading Report with container information and pictures will be sent to you !!

 

 

 Concrete Admixture Polypropylene Monofilament Fiber.jpg