Concrete Admixtures Monofilament Polypropylene Fiber 4mm 6mm 12mm 18mm 24mm Basic Info
Model NO.: Elite
Material: 100% Polypropylene
Width: as Per Your Request
Structure: Synthetic Carbon Chain
Length: Times of 4mm/6mm with 1mm More or Less
Fiber Diameter: 20-30um
Melting Point(C Deg. ): 160-170
Polypropylene Staple Fiber Crack Elongation: 20+/-5%
Certificate: CE/ ISO
Transport Package: 20kg/Plastic Woven Bag, 9ton/20′gp, 20ton/40′hq
Fiber Type: Staple
Polypropylene Staple Fiber Function: Reinforce Fiber
Product Name: Monofilament Polypropylene Fiber
Raw Material: 100% Virgin Polypropylene
Tensile Strength: 450MPa Min
Polypropylene Staple Fiber Acid &Alkali Resistance: Strong
HS Code: 5603949090
Concrete Admixtures Monofilament Polypropylene Fiber 4mm 6mm 12mm 18mm 24mm Product Description
Polypropylene monofilament Fiber PROPERTIES:
Our PP fiber monofilament was produced by referring foreign advanced technology for fibers pinning, modified by adding functional additive and special surface-treating. Mixing into cement concrete, it has many advantages such as good dispersing, better water affinity, strong linking force. It is suited to reinforce and crack-resist to every kinds of cement concrete and mortar, specially used in engineering of building surface, floor, wall etc...
Polypropylene monofilament Fiber APPLICATIONS:
1. Concrete Admixtures Monofilament Polypropylene Fiber 4mm 6mm 12mm 18mm 24mm Functions:
Resist to shrink & crack Increase seepage resistance
Increase friction resistance Increase freezing & thawing resistance
Improve tendons protection Replace steel net (using in plastering)
Prevent mortar split and crackle expansion
Increase impact resistance and peeling resistance
2,Polypropylene monofilament Fiber Features:
A). No agglomeration and easily spread around in mortar or concrete. Guarantee the property of crack resistance effectively
B). Apply conveniently. No need to change the proportion of mortar, and just put the fibers into the mortar mixture and stir for a moment after adding water.
C). Has fine economic property. The equivalent dia. Of polypropylene monofilament is only φ0.02mm, so the ratio of dia. And surface is high and on the basis of crack resistance, it can reduce the amount (0.6kg/m 3 ) and cut down the cost effectively.
D). Be better to plaster. Because a great number of thin fibers spread into mortar evenly, so the plastering is much easier and this can improve the binding strength between surface and base.
E). The fiber has stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.
3. Polypropylene monofilament Fiber Applications:
A). Suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.
4. Polypropylene monofilament Fiber Instruction:
A). Dosage: For resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar Is enough, and for increasing reinforce and seepage resist application 1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely. Also it can be mixed with cement and other aggregates in advance, stirring by adding water at worksite before construction.
Polypropylene monofilament Fiber brief specification:
|Raw Material :||Polypropylene||Crack Elongation:||20+/-5%|
|Fiber Type :||monofilament||Fiber Diameter:||20um-30um|
|Melting Point(C Deg.) :||160 - 170||Density(g/cm3) :||0.91+/-0.01|
|Acid &Alkali Resistance :||Strong||Tensile Strength(MPa):||450 min.|
|Length:||times of 4mm/6MM with 1mm|
more or less
|water absorbency :||NO|
Concrete Admixtures Monofilament Polypropylene Fiber 4mm 6mm 12mm 18mm 24mm Polypropylene monofilament Fiber Packing:
1,600g or 900g or 1000g / pe film bag, 18kg or 20kg / Plastic woven
2,600g or 900g or 1000g / Water soluble Paper bag, 18kg/carton,
3, ,600g or 900g or 1000g / Water soluble Paper bag, 18kg/Plastic Woven bag, 7tons/1x20`gp,14ton/40'gp, 18tons/40'HQ
4,Other Packing Quantity can negotiate
- Three Issues Limiting Textile Enter...
- Chemical Fiber Textile Industry And...
- Functional Fabrics And Wide Space
- Ecological Fiber Has Great Potential
- Difference Or Chemical Fiber Indust...
- Mechanical Substitution Of The Text...
- Textile Machinery And Machinery Sub...
- Change Building On Exports Textiles...
- Textile Merchant Which Changes Are ...
- Textile Fabrics Mildew Common Clean...
- Polyvinyl Alcohol Fibers Synthetic ...
- 15D*64mm Hollow Conjugated Siliconi...
- 8mm 12mm 16mm 18mm 20mm 24mm 28mm P...
- 100% Virgin Polypropylene PP Fiber ...
- 8mm 12mm 16mm 18mm 20mm 24mm 28mm P...
- Polypropylene PP Fiber Synthetic Mi...
- Regenerated Polyester Staple Fiber ...
- High Tenacity and High Modulus PVA ...
- China Producer Polyester Fiber with...
- 7D (15D) *64mm Wadding Polyester Fi...